Verwandte Artikel zu SWELLING RESISTANCE OF NANO POLYMER NANOCOMPOSITE
Inhaltsangabe
The ethylene-propylene-diene monomer/styrene-butadiene rubber (EPDM/SBR)-nanosilica (SiO2) nanocomposite was prepared. The 0–10 parts per hundred rubber (phr) of SiO2 with EPDM/SBR was mixed on a two-roll mill. The effect of nanosilica (0–10 phr), and silane coupling agent (bis(triethoxysilylpropyl)-tetrasulphide) (TESPT) on the curing characteristics, mechanical properties, rebound resilience, compression characteristics, abrasion, swelling property and morphological characteristics of the EPDM/SBR-SiO2 nanocomposites was investigated and studied. From the results, it was clear that the mechanical, wear and swelling properties steps-up with increase in the content of nanosilica particles in it. The addition of TESPT enhances the properties of the nanocomposites to a greater extent. From the analysis, it was clear that the effect of nanosilica concentration in the rubber composite with TESPT was found to be superior compared to nanocomposites without it.
Die Inhaltsangabe kann sich auf eine andere Ausgabe dieses Titels beziehen.
Neu kaufen
Diesen Artikel anzeigen
EUR 43,90
Gratis für den Versand innerhalb von/der Deutschland
Versandziele, Kosten & DauerSuchergebnisse für SWELLING RESISTANCE OF NANO POLYMER NANOCOMPOSITE
Foto des Verkäufers
SWELLING RESISTANCE OF NANO POLYMER NANOCOMPOSITE
Verlag:
LAP LAMBERT Academic Publishing Jun 2024, 2024
ISBN 10: 6207652045
ISBN 13: 9786207652044
Neu
Taschenbuch
Anbieter: buchversandmimpf2000, Emtmannsberg, BAYE, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. Neuware -The ethylene-propylene-diene monomer/styrene-butadiene rubber (EPDM/SBR)-nanosilica (SiO2) nanocomposite was prepared. The 0¿10 parts per hundred rubber (phr) of SiO2 with EPDM/SBR was mixed on a two-roll mill. The effect of nanosilica (0¿10 phr), and silane coupling agent (bis(triethoxysilylpropyl)-tetrasulphide) (TESPT) on the curing characteristics, mechanical properties, rebound resilience, compression characteristics, abrasion, swelling property and morphological characteristics of the EPDM/SBR-SiO2 nanocomposites was investigated and studied. From the results, it was clear that the mechanical, wear and swelling properties steps-up with increase in the content of nanosilica particles in it. The addition of TESPT enhances the properties of the nanocomposites to a greater extent. From the analysis, it was clear that the effect of nanosilica concentration in the rubber composite with TESPT was found to be superior compared to nanocomposites without it.Books on Demand GmbH, Überseering 33, 22297 Hamburg 52 pp. Englisch. Artikel-Nr. 9786207652044
Anzahl: 2 verfügbar