Verwandte Artikel zu Study of Wet Fastness after Moulding on Nylon Fabric...
Inhaltsangabe
The after-moulding wet fastness of nylon fabrics was investigated in this study. The performance of nylon 6 and nylon 66 was compared by preparing both fabrics under exactly the same conditions. The after-moulding wet fastness of non-metallised acid dyes of different molecular sizes was also compared in this study. Nylon 6 and 66 fabrics were dyed with 3 sets of dyes, namely, NYLOSAN E, NYLOSAN N and NYLOSAN S dyes of different molecular sizes at 105ºC for 10-20 minutes depending on the shade. Then the fabrics were subjected to fixation at 70ºC for 25 minutes. Finished fabrics were then moulded by contour moulding machine at 195ºC for 60s. AATCC wet colourfastness tests were done and the performance of samples was compared.
Die Inhaltsangabe kann sich auf eine andere Ausgabe dieses Titels beziehen.
Reseña del editor
The after-moulding wet fastness of nylon fabrics was investigated in this study. The performance of nylon 6 and nylon 66 was compared by preparing both fabrics under exactly the same conditions. The after-moulding wet fastness of non-metallised acid dyes of different molecular sizes was also compared in this study. Nylon 6 and 66 fabrics were dyed with 3 sets of dyes, namely, NYLOSAN E, NYLOSAN N and NYLOSAN S dyes of different molecular sizes at 105ºC for 10-20 minutes depending on the shade. Then the fabrics were subjected to fixation at 70ºC for 25 minutes. Finished fabrics were then moulded by contour moulding machine at 195ºC for 60s. AATCC wet colourfastness tests were done and the performance of samples was compared.
Biografía del autor
Dr. Kan graduated from Hong Kong Polytechnic University with BSc and PhD in Textile Chemistry. He had worked in private and public sectors in the area of textile evaluation and safety and health management for more than five years before joining the Institute. His teaching and research area are in coloration and finishing.
„Über diesen Titel“ kann sich auf eine andere Ausgabe dieses Titels beziehen.
Neu kaufen
Diesen Artikel anzeigen
EUR 23,90
Gratis für den Versand innerhalb von/der Deutschland
Versandziele, Kosten & DauerSuchergebnisse für Study of Wet Fastness after Moulding on Nylon Fabric...
Foto des Verkäufers
Study of Wet Fastness after Moulding on Nylon Fabric with Acid Dyes
Verlag:
LAP LAMBERT Academic Publishing Jun 2017, 2017
ISBN 10: 333034508X
ISBN 13: 9783330345089
Neu
Taschenbuch
Anbieter: buchversandmimpf2000, Emtmannsberg, BAYE, Deutschland
Verkäuferbewertung 5 von 5 Sternen
Taschenbuch. Zustand: Neu. Neuware -The after-moulding wet fastness of nylon fabrics was investigated in this study. The performance of nylon 6 and nylon 66 was compared by preparing both fabrics under exactly the same conditions. The after-moulding wet fastness of non-metallised acid dyes of different molecular sizes was also compared in this study. Nylon 6 and 66 fabrics were dyed with 3 sets of dyes, namely, NYLOSAN E, NYLOSAN N and NYLOSAN S dyes of different molecular sizes at 105ºC for 10-20 minutes depending on the shade. Then the fabrics were subjected to fixation at 70ºC for 25 minutes. Finished fabrics were then moulded by contour moulding machine at 195ºC for 60s. AATCC wet colourfastness tests were done and the performance of samples was compared.Books on Demand GmbH, Überseering 33, 22297 Hamburg 60 pp. Englisch. Artikel-Nr. 9783330345089
Anzahl: 2 verfügbar
Beispielbild für diese ISBN
Study of Wet Fastness after Moulding on Nylon Fabric with Acid Dyes
Verlag:
LAP LAMBERT Academic Publishing, 2017
ISBN 10: 333034508X
ISBN 13: 9783330345089
Neu
Paperback
Anbieter: Revaluation Books, Exeter, Vereinigtes Königreich
Verkäuferbewertung 5 von 5 Sternen
Paperback. Zustand: Brand New. 60 pages. 8.66x5.91x0.14 inches. In Stock. Artikel-Nr. 333034508X
Anzahl: 1 verfügbar