Ceramic matrix composites (CMCs) can withstand higher temperatures, reduce cooling airflow, improve turbine efficiency, and greatly reduce structural mass compared to the high temperature alloys. This book focuses on the matrix first/multiple cracking, crack opening and closure behavior in CMCs at high temperatures.

 

While conducting in situ experimental observations to analyze the damage mechanisms and failure modes, the author develops micromechanical damage models and constitutive models to predict the first matrix cracking stress, multiple matrix cracking density, matrix crack opening displacement, and cracking closure stress at high temperatures. The effects of composite’s constituent properties, stress level, and ambient temperature on matrix cracking, opening, and closure are also discussed.

 

This book will help material scientists and engineering designers to understand and master the matrix cracking and closure behavior of fiber-reinforced CMCs.

Die Inhaltsangabe kann sich auf eine andere Ausgabe dieses Titels beziehen.

Über die Autorin bzw. den Autor

Longbiao Li is a lecturer at College of Civil Aviation, Nanjing University of Aeronautics and Astronautics. Dr. Li’s research focuses on the vibration, fatigue, damage, fracture, reliability, safety and durability of aircraft and aero engines. In this research area, he is the first author of 204 SCI journal publications (59 JCR Q1), 11 monographs, 4 edited books, 4 textbooks, 3 book chapters, 33 Chinese patents, 2 US patents, 2 Chinese software copyrights, and more than 30 refereed conference proceedings. He has been involved in different projects related to structural damage, reliability, and airworthiness design for aircraft and aero engines, supported by the Natural Science Foundation of China, COMAC Company, and AECC Commercial Aircraft Engine Company.

Von der hinteren Coverseite

This book focuses on the matrix first/multiple cracking, crack opening and closure behavior in Ceramic-matrix composites (CMCs) at high temperatures.

„Über diesen Titel“ kann sich auf eine andere Ausgabe dieses Titels beziehen.

Verlag
CRC Press
Erscheinungsdatum
2023
Sprache
Englisch
ISBN 10 
103263751X
ISBN 13 
9781032637518
Einband
Gebundene Ausgabe
Anzahl der Seiten
144
Kontakt zum Hersteller
preigu GmbH & Co. KG
mail@preigu.de

Lengericher Landstr. 19
Osnabrück
Niedersachsen
49078
Deutschland